biodegradable plastic resin for film

biggest factory with rich export experience; High biodegradability: upto 100% in 3 months. best price with high quality.  

Product Name: BIODEGRADABLE RESIN STARCH

Product Model: BOR-Z-501F (a special type of blown film resin)

The main ingredients: starch ≥ 40% ≥ 12%; grease; PE ≥ 30%; the various auxiliaries ≥ 18%.

Features: light yellow, slightly starch flavor, easy to absorb moisture, easily decomposed by

microorganisms, natural antistatic, cylindrical or round particulate processing temperature

lower than ordinary plastic, coloring good performance can be directly processed into

products, not The need to add PE, PP, PVA, EVA and other polyolefin materials can be

processed into products.

Technical indicators:

Name BOR-Z-501F Test Item Test methods Unit Standard

Exterior (Q/320113SSD001-2002) Pale yellow

Density (GB1033)g/cm3 0.98-1.05

Moisture (Q/320113SSD001-2002)% 0.6-1.2

Melt flow rate (GB3682)g/10min 0-2

Rush strength(GB1040)MPa ≥ 12

Elongation at break (GB1040)% ≥ 250

Starch content (Q/320113SSD001-2002) % ≥ 45

Biological content (Q/320113SSD001-2002 )%≥ 55

Hexane extracts (GB/T500)9.58 %≤ 4.0

Softening Point (GB/1633 )°C> 65

Suggested Applications: all kinds of anti-static film products, such as: electronic products

packaging film, car interior packaging film, packaging film of home appliances, dust-proof

packaging film, medical film, agricultural film, shopping bags, vest bags, paper bags, filter

disposable green plastic bags, storage bags, garbage bags, bags on roll, disposable gloves,

tablecloths, aprons, raincoats products.

Processing equipment; common blown film machine, casting machine, bag making machine,

printing press sealing machine can produce.

Process:Film blowing machine try to choose the Screw aspect ratio larger L / D ≥ 25 1:1; blowing die

with the diameter of the tube membrane sheets than> 1:3, so that is conducive to the

plasticizing and improve product quality and yield.

This product blown film and LDPE blown film material blend blown film, HDPE blends blown

film need to add a certain proportion of LLDPE or LDPE (MI 4)

3 the blown film made of just due to severe dehydration, the feel more brittle, lower tensile

strength, for 24 hours, enhance tensile

Strength, tear strength, elongation is significantly increased, so the blown film should be

placed after a period of time and then printing bag.

4 can be blown more than 0.006mm film products.

Note:

1.Due to the starch content, easy to absorb, store sealed packaging, pay attention to

moisture.

2, such as the product water exceeded, should be dried after use, drying time is 2 hours, the

temperature of 105 ° C.

Processing temperature lower than that of PE 5-10 °C, processing film, the hopper the thick

corn flavor is the best temperature.

Microbial survival environment, easily decomposed into soil friendly substances.

Country/RegionAccount TypeCompany NameCompany Name in ChineseTime ZoneProvince/CityAddressZip/Post CodeTelephoneFaxWebsite

China

Supplier

Qingdao Central Co., Ltd

(GMT+08:00) Beijing, Hong Kong

Shandong ,Qingdao

Tianbao International Building, Ginza 15 Floor, Haier Road 61st, Qingdao, Shandong, China

266061

86-532-55576181

86-532-55576181

http://www.centralqd.com

biodegradable plastic resin for film